Yes, I've tried a number of times to get the rods to 'weld' but not managed it. It's been a while now since I last tried it but from memory there's a number of reasons why that may be the case - I may have useless technique, I may not have cleaned everything sufficiently, I may have been getting / able to get the workpieces hot enough or the alloy I was trying to repair may not be suitable. Again from memory, the last thing I tried it on was some cracked Kawasaki alloy manifold clamps. I couldn't replace them (unobtainable) but I didn't want to ruin them either.
The rods are more like high temp soldering than true welding and it was getting them to melt and run into the alloy that was the issue. Like normal soldering you can't just blob the stuff on, it doesn't take. The alloy needs to be clean and hot - much hotter than normal soldering but I was worried I could overheat the whole thing and just end up with a puddle on the bench. Aluminium doesn't give you any warning - like glowing red etc, so you have to use other methods. I have an I.R. thermometer but I'm not sure it goes high enough (?).
It was on my list of things to revisit but, prior to your post, fairly well down it.
|